| FR515 NC010 |
15% Glass reinforced, V-0 at 0.8 mm (0.031 inch) 本色 |
DuPont? Rynite? FR515 BK507 PET
| Categories: |
Polymer;Thermoplastic;Polyester, TP;Polyethylene Terephthalate (PET);Polyethylene Terephthalate (PET), 20% Glass Reinforced
|
| Material Notes: |
Rynite? FR515 BK507 is a flame retardant 15% glass reinforced modified polyethtylene terephthalate. Recognized by UL as UL94V-0 at 0.8mm(0.03in). Has a 140C temp index. Excellent balance of electrical and mechanical prop. High temp. resistance and flow.
Information provided by DuPont |
Physical PropertiesMetricEnglishCommentsMechanical PropertiesMetricEnglishCommentsElectrical PropertiesMetricEnglishCommentsThermal PropertiesMetricEnglishCommentsProcessing PropertiesMetricEnglishComments
| Density | 1.55g/cc | 0.0560lb/in3 | ISO 1183 |
| Filler Content | 15.0 % | 15.0 % | |
|
Tensile Strength at Break |
100MPa @Temperature 23.0 °C |
14500psi @Temperature 73.4 °F |
ISO 527 |
|
125MPa @Temperature -40.0 °C |
18100psi @Temperature -40.0 °F |
ISO 527 | |
|
Elongation at Break |
2.00 % @Temperature -40.0 °C |
2.00 % @Temperature -40.0 °F |
ISO 527 |
|
2.20 % @Temperature 23.0 °C |
2.20 % @Temperature 73.4 °F |
ISO 527 | |
|
Tensile Modulus |
3.59GPa @Temperature 150 °C |
521ksi @Temperature 302 °F |
ISO 527 |
|
6.135GPa @Temperature 23.0 °C |
889.8ksi @Temperature 73.4 °F |
ISO 527 | |
|
7.721GPa @Temperature -40.0 °C |
1120ksi @Temperature -40.0 °F |
ISO 527 | |
|
Flexural Modulus |
6.00GPa @Temperature 23.0 °C |
870ksi @Temperature 73.4 °F |
ISO 178 |
|
6.737GPa @Temperature -40.0 °C |
977.1ksi @Temperature -40.0 °F |
ISO 178 | |
|
Flexural Strength |
160MPa @Temperature 23.0 °C |
23200psi @Temperature 73.4 °F |
ISO 178 |
|
180MPa @Temperature -40.0 °C |
26100psi @Temperature -40.0 °F |
ISO 178 | |
|
Izod Impact, Unnotched (ISO) |
18.0kJ/m2 @Temperature -40.0 °C |
8.57ft-lb/in2 @Temperature -40.0 °F |
ISO 180/1U |
|
26.0kJ/m2 @Temperature 23.0 °C |
12.4ft-lb/in2 @Temperature 73.4 °F |
ISO 180/1U | |
|
Charpy Impact Unnotched |
2.00J/cm2 @Temperature -40.0 °C |
9.52ft-lb/in2 @Temperature -40.0 °F |
ISO 179/1eU |
|
3.20J/cm2 @Temperature 23.0 °C |
15.2ft-lb/in2 @Temperature 73.4 °F |
ISO 179/1eU | |
|
Charpy Impact, Notched |
0.600J/cm2 @Temperature -40.0 °C |
2.86ft-lb/in2 @Temperature -40.0 °F |
ISO 179/1eA |
|
0.620J/cm2 @Temperature 23.0 °C |
2.95ft-lb/in2 @Temperature 73.4 °F |
ISO 179/1eA | |
|
Izod Impact, Notched (ISO) |
5.00kJ/m2 @Temperature -40.0 °C |
2.38ft-lb/in2 @Temperature -40.0 °F |
ISO 180/1A |
|
5.50kJ/m2 @Temperature 23.0 °C |
2.62ft-lb/in2 @Temperature 73.4 °F |
ISO 180/1A | |
| Comparative Tracking Index |
175-250V @Temperature 23.0 °C |
175-250V @Temperature 73.4 °F |
PLC 3; UL 746A |
|
CTE, linear, Parallel to Flow |
19.0μm/m-°C @Temperature 55.0 - 160 °C |
10.6μin/in-°F @Temperature 131 - 320 °F |
ISO 11359-1/-2 |
|
29.0μm/m-°C @Temperature 23.0 - 55.0 °C |
16.1μin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1/-2 | |
|
33.0μm/m-°C @Temperature -40.0 - 23.0 °C |
18.3μin/in-°F @Temperature -40.0 - 73.4 °F |
ISO 11359-1/-2 | |
|
CTE, linear, Transverse to Flow |
74.0μm/m-°C @Temperature -40.0 - 23.0 °C |
41.1μin/in-°F @Temperature -40.0 - 73.4 °F |
ISO 11359-1/-2 |
|
95.0μm/m-°C @Temperature 23.0 - 55.0 °C |
52.8μin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1/-2 | |
|
125μm/m-°C @Temperature 55.0 - 160 °C |
69.4μin/in-°F @Temperature 131 - 320 °F |
ISO 11359-1/-2 | |
| Melting Point | 254°C | 489°F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 238°C | 460°F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 200°C | 392°F | ISO 75-1/-2 |
| Flammability, UL94 | 5VA | 5VA | IEC 60695-11-20 |
|
|
V-0 @Thickness 0.860 mm |
V-0 @Thickness 0.0339 in |
IEC 60695-11-10 |
|
V-0 @Thickness 3.00 mm |
V-0 @Thickness 0.118 in |
IEC 60695-11-10 | |
|
V-0 @Thickness 3.00 mm |
V-0 @Thickness 0.118 in |
UL94 | |
|
V-0 @Thickness 0.860 mm |
V-0 @Thickness 0.0339 in |
UL94 | |
|
5VA @Thickness >=1.50 mm |
5VA @Thickness >=0.0591 in |
5V; IEC 60695-11-20 | |
|
5VA @Thickness 1.50 mm |
5VA @Thickness 0.0591 in |
IEC 60695-11-10 | |
|
5VA @Thickness 1.50 mm |
5VA @Thickness 0.0591 in |
UL94 | |
| Melt Temperature | 280°C | 536°F | optimum |
| 270-290°C | 518-554°F | ||
| Mold Temperature | >=95.0°C | >=203°F | |
| 110°C | 230°F | Optimum | |
| Drying Temperature | 120°C | 248°F | |
| Dry Time | 4.00hour | 4.00hour | |
| Moisture Content | <= 0.0200 % | <= 0.0200 % | |
免責(zé)聲明：（1）以上所展示的信息由企業(yè)自行提供，內(nèi)容的真實(shí)性、準(zhǔn)確性和合法性由發(fā)布企業(yè)負(fù)責(zé)，環(huán)球塑化網(wǎng)對(duì)此不承擔(dān)任何保證責(zé)任。我們?cè)瓌t上建議您優(yōu)先選擇“塑企通”會(huì)員合作! （2）同時(shí)我們鄭重提醒各位買/賣家，交易前請(qǐng)?jiān)敿?xì)核實(shí)對(duì)方身份，切勿隨意打款或發(fā)貨，謹(jǐn)防上當(dāng)受騙。如發(fā)現(xiàn)虛假信息，請(qǐng)向環(huán)球塑化網(wǎng)舉報(bào)。