點(diǎn)擊圖片查看大圖
供應(yīng)蘇威 KetaSpire PEEK KT-820 GF13
供應(yīng)蘇威 KetaSpire PEEK KT-820 GF30
供應(yīng)蘇威 KetaSpire PEEK KT-820 NL
供應(yīng)蘇威 KetaSpire PEEK KT-820 SL10
供應(yīng)蘇威 KetaSpire PEEK KT-820 SL30
供應(yīng)蘇威 KetaSpire PEEK KT-820 SL45
供應(yīng)蘇威 KetaSpire PEEK KT-820
供應(yīng)蘇威 KetaSpire PEEK KT-820FP
供應(yīng)蘇威 KetaSpire PEEK KT-820P
供應(yīng)蘇威 KetaSpire PEEK KT-850
供應(yīng)蘇威 KetaSpire PEEK KT-850P
供應(yīng)蘇威 KetaSpire PEEK KT-851 NL
供應(yīng)蘇威 KetaSpire PEEK KT-851
供應(yīng)蘇威 KetaSpire PEEK KT-880 CF30
供應(yīng)蘇威 KetaSpire PEEK KT-880 GF30
供應(yīng)蘇威 KetaSpire PEEK KT-880 NL
供應(yīng)蘇威 KetaSpire PEEK KT-880
供應(yīng)蘇威 KetaSpire PEEK KT-880P 】
| Solvay Specialty Polymers KetaSpire? KT-820 CF30 Polyetheretherketone (PEEK), 30% Carbon Fiber | |||
|---|---|---|---|
| Categories: | Polymer; Thermoplastic; Polyketone; Polyetheretherketone (PEEK); Polyetheretherketone, PEEK, Carbon Fiber Filled | ||
| Material Notes: |
KetaSpire? KT-820 CF30 is the low-flow, 30% carbon-fiber reinforced grade of polyetheretherketone (PEEK). Carbon- fiber reinforcement of KetaSpire? PEEK provides the maximum levels of mechanical properties at temperatures approaching 300°C, and the lowest coefficient of linear thermal expansion within the KetaSpire? product family.
KetaSpire? PEEK is produced to the highest industry standards and is characterized by a distinct combination of properties, which include excellent wear resistance, best-in-class fatigue resistance, ease of melt processing, high purity, and excellent chemical resistance to organics, acids and bases. Features: Autoclave Sterilizable; E-beam Sterilizable; Ethylene Oxide Sterilizable; Fatigue Resistant; Flame Retardant; Good Chemical Resistance; Good Dimensional Stability; Good Sterilizability; Heat Sterilizable; High Heat Resistance; High Stiffness; High Strength; Radiation (Gamma) Resistant; Radiation Sterilizable; Radiotranslucent; Steam Resistant; Steam Sterilizable Uses: Automotive Applications; Connectors; Dental Applications; Electrical/Electronic Applications; Gears; Hospital Goods; Industrial Applications; Medical Devices; Medical/Healthcare Applications; Oil/Gas Applications; Pump Parts; Surgical Instruments; Thrust Washer Information provided by Solvay Specialty Polymers. |
||
| Vendors: |
Drake Plastics Ltd. Co. manufactures & stocks PEEK rod & plate for machined parts using Solvay Specialty Polymers KetaSpire resins. Drake also offers machined & injection molded parts using the latest technology. Drake practices lean techniques, producing products in single-piece flow ensuring that the first part is identical to the last.
Click here to view all available suppliers for this material. New suppliers have been added for this product during the past 60 days. Please click here if you are a supplier and would like information on how to add your listing to this material. |
||
|
|||
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in3 | ASTM D792 | ||
| Filler Content | 30.0 % | 30.0 % | Carbon Fiber | ||
| Water Absorption |
0.100 % @Time 86400 sec |
0.100 % @Time 24.0 hour |
ISO 62 | ||
| Viscosity |
920000 cP @Shear Rate 1000 1/s, Temperature 400 °C |
920000 cP @Shear Rate 1000 1/s, Temperature 752 °F |
Melt Viscosity; ASTM D3835 | ||
| Linear Mold Shrinkage, Flow |
0.000 - 0.00200 cm/cm @Thickness 3.18 mm |
0.000 - 0.00200 in/in @Thickness 0.125 in |
|||
| Linear Mold Shrinkage, Transverse |
0.0150 - 0.0170 cm/cm @Thickness 3.18 mm |
0.0150 - 0.0170 in/in @Thickness 0.125 in |
ASTM D955 | ||
| Melt Flow |
1.10 g/10 min @Load 2.16 kg, Temperature 400 °C |
1.10 g/10 min @Load 4.76 lb, Temperature 752 °F |
ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 105 | 105 | ASTM D785 | ||
| Hardness, Shore D | 92.0 | 92.0 | 1 sec; ASTM D2240 | ||
| Tensile Strength | 201 MPa | 29200 psi | ASTM D638 | ||
| Tensile Strength, Yield | 217 MPa | 31500 psi | 5 mm/min, Type 1A; ISO 527-2 | ||
| Elongation at Break | 2.00 % | 2.00 % | Type 1A, 5 mm/min; ISO 527-2 | ||
| 2.00 % | 2.00 % | 5 mm/min; ASTM D638 | |||
| Tensile Modulus | 19.7 GPa | 2860 ksi | 5 mm/min; ASTM D638 | ||
| 22.8 GPa | 3310 ksi | 1 mm/min, Type 1A; ISO 527-2 | |||
| Flexural Strength | 311 MPa | 45100 psi | ISO 178 | ||
| 317 MPa | 46000 psi | ASTM D790 | |||
| Flexural Modulus | 17.5 GPa | 2540 ksi | ASTM D790 | ||
| 20.5 GPa | 2970 ksi | ISO 178 | |||
| Compressive Strength | 173 MPa | 25100 psi | ASTM D695 | ||
| Poissons Ratio | 0.420 | 0.420 | ASTM E132 | ||
| Shear Strength | 95.1 MPa | 13800 psi | ASTM D732 | ||
| Izod Impact, Notched | 0.690 J/cm | 1.29 ft-lb/in | ASTM D256 | ||
| Izod Impact, Unnotched | 7.50 J/cm | 14.1 ft-lb/in | ASTM D256 | ||
| Izod Impact, Notched (ISO) | 10.0 kJ/m2 | 4.76 ft-lb/in2 | ISO 180 | ||
| Izod Impact, Unnotched (ISO) | 44.0 kJ/m2 | 20.9 ft-lb/in2 | ISO 180 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow |
5.20 μm/m-°C @Temperature -50.0 - 50.0 °C |
2.89 μin/in-°F @Temperature -58.0 - 122 °F |
1 | ||
Specific Heat Capacity 
|
1.13 J/g-°C @Temperature 50.0 °C |
0.270 BTU/lb-°F @Temperature 122 °F |
ASTM C351 | ||
|
1.62 J/g-°C @Temperature 200 °C |
0.387 BTU/lb-°F @Temperature 392 °F |
ASTM C351 | |||
| Thermal Conductivity | 0.370 W/m-K | 2.57 BTU-in/hr-ft2-°F | ASTM C177 | ||
| Melting Point | 340 °C | 644 °F | ASTM D3418 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 315 °C | 599 °F | Annealed; ASTM D648 | ||
| Glass Transition Temp, Tg | 150 °C | 302 °F | DSC | ||
| Flammability, UL94 |
V-0 @Thickness 0.800 - 1.60 mm |
V-0 @Thickness 0.0315 - 0.0630 in |
|||
| Processing Properties | Metric | English | Comments | ||
| Rear Barrel Temperature | 365 °C | 689 °F | |||
| Middle Barrel Temperature | 370 °C | 698 °F | |||
| Front Barrel Temperature | 375 °C | 707 °F | |||
| Nozzle Temperature | 380 °C | 716 °F | |||
| Mold Temperature | 175 - 205 °C | 347 - 401 °F | |||
| Drying Temperature |
150 °C @Time 14400 sec |
302 °F @Time 4.00 hour |
|||
|
De |
|||||
| Availability | Africa & Middle East | ||||
| Asia Pacific | |||||
| Europe | |||||
| Latin America | |||||
| North America | |||||
| Color | Black | ||||
| Form | Pellets | ||||
| Injection Rate | Fast | ||||
| Processing Technique | Injection Molding; Machining; Profile Extrusion | ||||
| RoHS Compliance | RoHS Compliant | ||||
| Screw Compression Ratio | 2.5:1.0 to 3.5:1.0 | ||||