TYPICAL PROPERTIES (1)
|
|
MECHANICAL
|
Value
|
Unit
|
Standard
|
|
Tensile Stress, yld, Type I, 50 mm/min
|
610
|
kgf/cm2
|
ASTM D 638
|
|
Tensile Stress, brk, Type I, 50 mm/min
|
610
|
kgf/cm2
|
ASTM D 638
|
|
Tensile Strain, yld, Type I, 50 mm/min
|
7
|
%
|
ASTM D 638
|
|
Tensile Strain, brk, Type I, 50 mm/min
|
15
|
%
|
ASTM D 638
|
|
Tensile Modulus, 50 mm/min
|
25400
|
kgf/cm2
|
ASTM D 638
|
|
Tensile Stress, yield, 50 mm/min
|
60
|
MPa
|
ISO 527
|
|
Tensile Stress, break, 50 mm/min
|
60
|
MPa
|
ISO 527
|
|
Tensile Strain, yield, 50 mm/min
|
10
|
%
|
ISO 527
|
|
Tensile Strain, break, 50 mm/min
|
15
|
%
|
ISO 527
|
|
Tensile Modulus, 1 mm/min
|
2550
|
MPa
|
ISO 527
|
|
Flexural Stress, yield, 2 mm/min
|
85
|
MPa
|
ISO 178
|
|
Flexural Modulus, 2 mm/min
|
2400
|
MPa
|
ISO 178
|
|
Hardness, H358/30
|
145
|
MPa
|
ISO 2039-1
|
|
Hardness, Rockwell R
|
117
|
-
|
ISO 2039-2
|
|
IMPACT
|
Value
|
Unit
|
Standard
|
|
Charpy Impact, unnotched, 23°C
|
NB
|
kJ/m2
|
ISO 179/2C
|
|
Charpy Impact, unnotched, -30°C
|
80
|
kJ/m2
|
ISO 179/2C
|
|
Izod Impact, unnotched, 23°C
|
NB
|
cm-kgf/cm
|
ASTM D 4812
|
|
Izod Impact, unnotched, -30°C
|
NB
|
cm-kgf/cm
|
ASTM D 4812
|
|
Izod Impact, notched, 23°C
|
3
|
cm-kgf/cm
|
ASTM D 256
|
|
Izod Impact, notched, 0°C
|
3
|
cm-kgf/cm
|
ASTM D 256
|
|
Izod Impact, notched, -30°C
|
3
|
cm-kgf/cm
|
ASTM D 256
|
|
Izod Impact, unnotched 80*10*4 +23°C
|
NB
|
kJ/m2
|
ISO 180/1U
|
|
Izod Impact, unnotched 80*10*4 -30°C
|
100
|
kJ/m2
|
ISO 180/1U
|
|
Izod Impact, notched 80*10*4 +23°C
|
4
|
kJ/m2
|
ISO 180/1A
|
|
Izod Impact, notched 80*10*4 0°C
|
4
|
kJ/m2
|
ISO 180/1A
|
|
Izod Impact, notched 80*10*4 -30°C
|
4
|
kJ/m2
|
ISO 180/1A
|
|
Charpy Impact, notched, 23°C
|
4
|
kJ/m2
|
ISO 179/2C
|
|
Charpy Impact, notched, -30°C
|
4
|
kJ/m2
|
ISO 179/2C
|
|
THERMAL
|
Value
|
Unit
|
Standard
|
|
Vicat Softening Temp, Rate A/50
|
220
|
°C
|
ASTM D 1525
|
|
Vicat Softening Temp, Rate B/50
|
185
|
°C
|
ASTM D 1525
|
|
Ball Pressure Test, 125°C +/- 2°C
|
PASSES
|
-
|
IEC 60695-10-2
|
|
Vicat Softening Temp, Rate A/50
|
220
|
°C
|
ISO 306
|
|
Vicat Softening Temp, Rate B/50
|
185
|
°C
|
ISO 306
|
|
Vicat Softening Temp, Rate B/120
|
185
|
°C
|
ISO 306
|
|
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm
|
150
|
°C
|
ISO 75/Bf
|
|
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm
|
50
|
°C
|
ISO 75/Af
|
|
PHYSICAL
|
Value
|
Unit
|
Standard
|
|
Specific Gravity
|
1.31
|
-
|
ASTM D 792
|
|
Mold Shrinkage on Tensile Bar, flow (2) (5)
|
2 - 2.6
|
%
|
SABIC Method
|
|
Mold Shrinkage on Tensile Bar, xflow (2) (5)
|
0.9 - 1.8
|
%
|
SABIC Method
|
|
Density
|
1.31
|
g/cm3
|
ISO 1183
|
|
Water Absorption, (23°C/sat)
|
0.34
|
%
|
ISO 62
|
|
Moisture Absorption (23°C / 50% RH)
|
0.08
|
%
|
ISO 62
|
|
Melt Volume Rate, MVR at 250°C/2.16 kg
|
20
|
cm3/10 min
|
ISO 1133
|
|
Melt Volume Rate, MVR at 250°C/5.0 kg
|
50
|
cm3/10 min
|
ISO 1133
|
|
Melt Viscosity, 260°C, 1500 sec-1
|
165
|
Pa-s
|
ISO 11443
|
點(diǎn)擊圖片查看大圖
免責(zé)聲明：（1）以上所展示的信息由企業(yè)自行提供，內(nèi)容的真實(shí)性、準(zhǔn)確性和合法性由發(fā)布企業(yè)負(fù)責(zé)，環(huán)球塑化網(wǎng)對(duì)此不承擔(dān)任何保證責(zé)任。我們?cè)瓌t上建議您優(yōu)先選擇“塑企通”會(huì)員合作! （2）同時(shí)我們鄭重提醒各位買(mǎi)/賣(mài)家，交易前請(qǐng)?jiān)敿?xì)核實(shí)對(duì)方身份，切勿隨意打款或發(fā)貨，謹(jǐn)防上當(dāng)受騙。如發(fā)現(xiàn)虛假信息，請(qǐng)向環(huán)球塑化網(wǎng)舉報(bào)。