POM/美國杜邦/988P 均聚甲醛 耐高溫 pom工程塑料
產(chǎn)品參數(shù)
| 性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | ||
| 基本性能 | 吸水率 | 24小時浸漬 | ASTM D-570 | 0.25 | % | |
| 吸水率 | 50%相對濕度 | ASTM D-570 | 0.22 | % | ||
| 吸水率 | 浸漬平衡點 | ASTM D-570 | 0.90 | % | ||
| 物理性能 | 模縮率 | 1.8-2.0 | % | |||
| 比重 | ASTM D-792 | 1.42 | ||||
| 機械性能 | 破裂點拉伸變形量 | 100℃ | ASTM D-638 | >260 | % | |
| 撓曲系數(shù) | 100℃ | ASTM D-790 | 1030 | MPa | ||
| 拉伸強度 | 100℃ | ASTM D-638 | 36 | MPa | ||
| 彈性系數(shù) | 23℃ | ASTM D-638 | 3640 | MPa | ||
| 拉伸強度 | 70℃ | ASTM D-638 | 48 | MPa | ||
| 壓縮應(yīng)力 | 23℃，10%變形 | ASTM D-695 | 121 | MPa | ||
| 埃佐沖擊試驗 | 缺口-40℃ | ASTM D-256 | 55 | J/m | ||
| 破裂點拉伸變形量 | 122℃ | ASTM D-638 | >260 | % | ||
| 破裂點拉伸變形量 | -55℃ | ASTM D-638 | 10 | % | ||
| 撓曲系數(shù) | 70℃ | ASTM D-790 | 1720 | MPa | ||
| 破裂點拉伸變形量 | 23℃ | ASTM D-638 | 25 | % | ||
| 洛氏硬度R | ASTM D-785 | 120 | ||||
| 撓曲變形強度 | 23℃ | ASTM D-790 | 97 | MPa | ||
| 撓曲系數(shù) | -55℃ | ASTM D-790 | 4730 | MPa | ||
| 拉伸強度 | 23℃ | ASTM D-638 | 69 | MPa | ||
| 抗剪強度 | 23℃ | ASTM D-732 | 66 | MPa | ||
| 撓曲系數(shù) | 23℃ | ASTM D-790 | 3220 | MPa | ||
| 洛氏硬度M | ASTM D-785 | 94 | ||||
| 撓曲疲勞忍耐限度 | 50%RH，23℃，106周期 | ASTM D-671 | 32 | MPa | ||
| 撓曲系數(shù) | 122℃ | ASTM D-790 | 755 | MPa | ||
| 破裂點拉伸變形量 | 70℃ | ASTM D-638 | 180 | % | ||
| 拉伸強度 | -55℃ | ASTM D-638 | 101 | MPa | ||
| 抗拉伸沖擊強度 | 23℃ | ASTM D-1822 | 250 | kj/m2 | ||
| 壓縮應(yīng)力 | 23℃，1%變形 | ASTM D-695 | 35 | MPa | ||
| 負(fù)載變形量 | 140kg/cm2,50℃ | ASTM D-621 | 0.5 | % | ||
| 埃佐沖擊試驗 | 無缺口23℃ | ASTM D-256 | 1620 | J/m | ||
| 拉伸強度 | 122℃ | ASTM D-638 | 26 | MPa | ||
| 埃佐沖擊試驗 | 23℃ | ASTM D-256 | 71 | J/m | ||
| 電氣性能 | 介電常數(shù) | 50%RH，23℃，102～106Hz | ASTM D-150 | 3.7 | Ohm-cm | |
| 介電因數(shù) | 50%RH，23℃，106Hz | ASTM D-150 | 0.005 | |||
| 介電強度 | 2.3mm | ASTM D-149 | 19.7 | Kv/mm | ||
| 抗電弧 | 3.1mm | ASTM D-495 | 220 | SEc | ||
| 容積電阻率 | 23℃，0.2%含水量 | ASTM D-257 |
|
Ohm-cm | ||
| 熱性能 | 線性熱膨脹系數(shù) | 104～160℃ | ASTM D-696 | 14.9 | 10-5m/m | |
| 線性熱膨脹系數(shù) | 60～104℃ | ASTM D-696 | 13.7 | 10-5m/m | ||
| 熔點 | ASTM D-2133 | 175 | ||||
| 熱畸變溫度 | 1.8MPa | ASTM D-648 | 136 | |||
| 線性熱膨脹系數(shù) | 29～60℃ | ASTM D-696 | 12.2 | 10-5m/m | ||
| 自燃性 | UL 94 | HB | ||||
| 熱傳導(dǎo)系數(shù) | 0.37 | W/mk | ||||
| 線性熱膨脹系數(shù) | -40～29 | ASTM D-696 | 10.4 | 10-5m/m | ||